Surface Preparation:

The Armor SX5000 WB should be applied to a completely clean and dry surface. If the surface was cleaned with water or pressure washed prior to application, allow the surface to dry for at least 24 hours before sealing. While the surface may appear dry and feel dry to touch, water below the surface trapped in the pores can cause the same issues. While pressure washing the surface is typically sufficient, spot treatment may be necessary for deep or older stains. If the surface is smooth troweled, or does not easily accept water, acid etching may be required prior to applying sealer. It is always suggested to apply the Armor SX5000 WB to a test area to verify absorption, coverage, compatibility, and project suitability.

The Armor SX5000 WB is designed specifically for unsealed concrete and masonry surfaces. Do not apply this product over a surface recently sealed with a water repellent sealer, or previously sealed with a film-forming sealer or coating.

Application:

A commercial pump sprayer is recommended to achieve the best coverage and results. Be sure the psi is no greater than 20. Use a .3-.5 GPM adjustable cone tip.

Apply the first coat of Armor SX5000 WB, ensuring the entire surface is evenly saturated. Broom out puddles until surface is penetrated. Second coat should be applied while the first coat is still wet.

Substrates sealed with Armor SX5000 WB may be coated with silicone emulsion paints and many oil based paints once the surface has had 72 hours to dry. Testing is always necessary and recommended to assure proper adhesion. Adhesion may be improved if the surface is pressure washed and allowed to dry prior to application. Armor SX5000 WB is not a paint primer. Adhesion of cementitious coatings, stucco, plaster, etc., may be adversely affected. These types of substrate treatments should be installed and allowed to fully cure before applying Armor SX5000 WB. Always test to verify compatibility.

Time of Day

The temperature of the air and surface must be 55-85 degrees F during application. If freezing conditions exist prior to application, it is highly recommended that the substrate be allowed to fully thaw. Should this recommendation not be followed, the product may not yield adequate protective properties.

Once applied, the surface should be kept dry for at least 24 hours.

Clean-Up

Use warm water and soap. Dispose of containers in accordance with local and federal regulations.

Product Removal

Armor SX5000 WB penetrates deep into to the surface. Removal is not recommended.

Porous Surfaces: Up to 175 FT2/gallon in one coat.

Smooth Surfaces (once properly prepped): Up to 200-225 FT2/gallon in one coat.

Coverage will vary depending on porosity, surface condition, application method, and the amount of material applied by the applicator. The above coverage rates are estimates and will vary. Two coats are suggested for even coverage and appearance.

The Armor SX5000 WB is designed specifically to be used on unsealed concrete, brick, natural stone, and masonry. The Armor SX5000 WB can’t be applied over any existing sealers, paints, or coatings.

The Armor SX5000 WB is a fantastic sealer for a variety of applications, including:

• Brick chimneys and brick walls
• Concrete, brick, natural stone, and paver patios and walkways
• Concrete, brick, and paver driveways
• Retaining walls and landscape curbing
• Concrete, brick, and stone building faces and accents
• Garage, basement, and warehouse floors
• Much more!

The Armor SX5000 WB is designed to work entirely below the surface. It chemically reacts to form a hydrophobic barrier in the pores. It will not change the look or color of the substrate, and it will not leave a visible surface film.

If you are looking for a wet look, low gloss, or high gloss, consider instead the Armor WL550 for a matte wet look, the Armor AR350 for a low gloss wet look, or the Armor AR500 for a high gloss wet look.

When properly applied, the Armor SX5000 WB can provide up to 7-10 years of life on an exterior surface before the need to recoat.

Water Bead: Surface water beading will not occur on all surfaces. While some surfaces may experience an instantaneous bead, others won’t experience a surface water bead at all. Surface water beading is not a sealer benefit. Surface water bead is caused from resin build-up on the surface. Once the resin build-up goes away, so will the bead. The Armor SX5000 WB is designed to work entirely below the surface so its benefits are made visible through performance. You will find sealed surfaces dry faster, are easier to clean, and experience less damage caused by freeze-thaw cycles and de-icing salts.